HYF002 HotSlip Polyolefin Shrink Film

HYF002 HotSlip High Speed Polyolefin Shrink film has all characteristics of our HYF001 Standard Polyolefin Shrink Film,It highlights the excellent Properties of sealing tension,When the film is packed at the high speed packing machine,good sealing tension would be a must,During the shrink Course,HYF002 is soft,transparent and fast sealing which is ideal for the high spead full automatic packing machine and widely used in collective and outside packaging of beverage,noodle, fast-food,milk and other industrial field.

The Datasheet of the HOTSLIP Polyolefin Shrink Film

ITEM UNIT TEST MOTHOD TYPICAL VALUE

Thickness Micron ASTM-D374 12 15 19 25

density g/cm3 ASTM-D1505 0.92 0.92 0.92 0.92

Tensile strength MD N/mm2 ASTM-D882-02 120 115 110 100

TD 115 110 110 95

Elongation at break MD % ASTM-D882-02 115 110 110 105

TD 105 100 100 95

Tear resistance MD N ASTM-D1938-03 3.5 4 4.5 6.7

TD 3.8 4 4.6 7.9

Seal strength N/15mm QBT23-58 10 11 12 14

C.O.F(Dynamic) ASTM-D1894-01 0.25 0.25 0.25 0.25

C.O.F(Static) ASTM-D1894-01 0.28 0.28 0.28 0.28

Haze % ASTM-D1003 2.5 2.5 2.5 2.5

MD/TD MD/TD MD/TD MD/TD

Free shrinkage rate 90℃ % ASTM-D2732-83 14/13 13/12 14/16 13/16

100℃ 25/28 26/24 27/24 26/23

110℃ 36/35 32/35 34/33 34/33

120℃ 60/60 60/60 60/60 60/60

130℃ 65/65 65/65 65/65 64/65

MD: Machine Direction TD: Transverse Direction

Note: The technical features of the products defined herein are given as typical values, representing our best judgement on the work done, They are guides for the use of the quoted films values and are not for use as the specification, users have to check-up that they are suitable with all the application as performance may vary with processing conditions, properties and performance are subject to change and Huayu keeps the right to modify the definition and properties of its products without prior notice

ITEM		UNIT	TEST MOTHOD	TYPICAL VALUE
Thickness		Micron	ASTM-D374	12	15	19	25
density		g/cm3	ASTM-D1505	0.92	0.92	0.92	0.92
Tensile strength	MD	N/mm2	ASTM-D882-02	120	115	110	100
Tensile strength	TD	N/mm2	ASTM-D882-02	115	110	110	95
Elongation at break	MD	%	ASTM-D882-02	115	110	110	105
Elongation at break	TD	%	ASTM-D882-02	105	100	100	95
Tear resistance	MD	N	ASTM-D1938-03	3.5	4	4.5	6.7
Tear resistance	TD	N	ASTM-D1938-03	3.8	4	4.6	7.9
Seal strength		N/15mm	QBT23-58	10	11	12	14
C.O.F(Dynamic)			ASTM-D1894-01	0.25	0.25	0.25	0.25
C.O.F(Static)			ASTM-D1894-01	0.28	0.28	0.28	0.28
Haze		%	ASTM-D1003	2.5	2.5	2.5	2.5
				MD/TD	MD/TD	MD/TD	MD/TD
Free shrinkage rate	90℃	%	ASTM-D2732-83	14/13	13/12	14/16	13/16
	100℃			25/28	26/24	27/24	26/23
	110℃			36/35	32/35	34/33	34/33
	120℃			60/60	60/60	60/60	60/60
	130℃			65/65	65/65	65/65	64/65
MD: Machine Direction TD: Transverse Direction
Note: The technical features of the products defined herein are given as typical values, representing our best judgement on the work done, They are guides for the use of the quoted films values and are not for use as the specification, users have to check-up that they are suitable with all the application as performance may vary with processing conditions, properties and performance are subject to change and Huayu keeps the right to modify the definition and properties of its products without prior notice

“Custom Work, Quality Service”

Your Primary Choice for Polyolefin Shrink Films Machines

Specialist POF machines Since 2006

Superior Quality3-5 Layer

Polyolefin Shrink Film Machine Manufacturer

Six 5 Layer Coextruded

Polyolefin Shrink Film Production Lines

High Intelligence

Polyolefin Shrink Film Slittering Machine

Advanced Technology 5 Layer

2400/2800/3500mm POF Film Machines

High Speed

Polyolefin Shrink Film Center Folding Machine

HYF002 HotSlip Polyolefin Shrink Film